This Article Full Text (PDF) References Alert me when this article is cited Alert me if a correction is posted Services Email this article to a friend Similar articles in this journal Alert me to new issues of the journal Add to Saved Citations Download to citation manager Request Permissions Request Reprints Add to My Marked Citations Citing Articles Citing Articles via HighWire Citing Articles via Google Scholar Citing Articles via Scopus Google Scholar Articles by Zhong, Y. Articles by Zhou, J. Search for Related Content Social Bookmarking                         What's this?

Study of Thermal and Hygrothermal Behaviors of Glass/Vinyl Ester Composites

Jianren Zhou

Department of Mechanical Engineering, Prairie View A&M University, Prairie View, TX 77446

Accelerated thermal and hygrothermal exposures were performed on S2-glass/vinyl ester composites. Effects of temperature, moisture, and exposure duration on some mechanical properties and microstructures of the composites were investigated, and thermal and hygrothermal degradation mechanisms were analyzed. It was found that the indentation resistance and compression strength of the composites showed an increase during a certain stage of the thermal exposure, which was attributed to the combined effects of thermal decission and an increase in crosslinking degree under elevated temperatures. Moisture, together with elevated temperature, had conspicuous deteriorating effects on some mechanical properties of the composites, and the property changes were more significant during the early stages of the hygrothermal exposure process. The influence of physical degradation induced by water was found to be less significant than that by chemical degradation resulting from resin decomposition. Microscopic observation showed that the matrix resin became fragmented and lost adhesion with fibers in the hygrothermally exposed composites.

Key Words: vinyl esters • polymer composites • hygrothermal behaviors • degradation • environmental durability

Journal of Reinforced Plastics and Composites, Vol. 18, No. 17, 1619-1629 (1999)
DOI: 10.1177/073168449901801706


CiteULike    Complore    Connotea    Del.icio.us    Digg    Reddit    Technorati    Twitter    What's this?

This article has been cited by other articles:

				Y. Yu, X. Yang, L. Wang, and H. Liu Hygrothermal Aging on Pultruded Carbon Fiber/Vinyl Ester Resin Composite for Sucker Rod Application Journal of Reinforced Plastics and Composites, January 1, 2006; 25(2): 149 - 160. [Abstract] [PDF]