This Article Full Text (PDF) References Alert me when this article is cited Alert me if a correction is posted Services Email this article to a friend Similar articles in this journal Alert me to new issues of the journal Add to Saved Citations Download to citation manager Request Permissions Request Reprints Add to My Marked Citations Citing Articles Citing Articles via Google Scholar Citing Articles via Scopus Google Scholar Articles by Gupta, N. Articles by Sankaran, S. Search for Related Content Social Bookmarking                         What's this?

On the Characterisation of Syntactic Foam Core Sandwich Composites for Compressive Properties

Department of Metallurgy, Centre for Advanced Studies, Polymer Composites Laboratory, Indian Institute of Science, Bangalore-560 012, India

S. Sankaran

Aeronautical Development Establishment, C. V Raman Nagar, Bangalore-560 093, India

Sandwich structures, especially those with honeycomb and grid structures as the core material, are very commonly employed in aircraft structures. There is an increasing use of closed-pore rigid syntactic foams as core materials in sandwich constructions because they possess a number of favourable properties. The syntactic foams, owing to their structure and formation, behave differently under compression compared to other traditionally used core materials. In the present study, therefore, syntactic foam core sandwich constructions are evaluated for their behaviour under compression in both edgewise and flatwise orientations. Further, the work characterises the relative performance of two sets of sandwich materials, one containing glass-epoxy and the other, glass/carbon hybrid-epoxy skins. As non-standard geometry test specimens were involved, only a comparative evaluation was contemplated in this approach. The experiments indicate that the nature of the reinforcement fabric in the skin has a bearing on the test results in edgewise orientation. Thus, the tendency towards initiation of vertical crack in the central plane of the core material, which is a typical fracture event in this kind of material, was found to occur after a delay for the specimens containing the glass fabric in the skin. Attempts are made to establish the correlation between observations made on the test specimen visually during the course of testing and the post-compression microscopic examinations of the fracture features.

Journal of Reinforced Plastics and Composites, Vol. 18, No. 14, 1347-1357 (1999)